industrial repair agent > super high temperature epoxy compound metal repair agent

super high temperature epoxy compound metal repair agent

BD1692 super high temperature wear resistant metal repair agent
epoxy compound

Performance features:
1.With higher bonding strength to metal substrates,the color can be kept the same as the pending-repair
substrates,the highest temperature resistance can reach to 600 degree.

2.With good construction manufacturability,the curing product is not shrinkage,with abrasion resistance,
corrosion resistance and aging resistance.

3.The material after curing has higher strength,can do various machining.

Product usage:
It’s the high temperature metal repair epoxy compound which compounded by modified high temperature resin
and high temperature curing agent,made of ceramic,metal etc.filling polymerization.The highest temperature
resistance is 600 degree,popular type,suitable for repairing various metal casting defect and repairing part abrasion,
corrosion and fracture,the material after repairing has higher strength,and excellent wear resistance,corrosion
resistance and aging resistance,can do various machining together with substrates.

Performance index:

BD1691 high temperature industrial metal repair agent physical and mechanical properties table:
Color	Bending strength (Mpa) GB1042-1999	Compressive strength (Mpa) GB/7124-2008	Shear strength (Mpa) GB/1041-2008	Hardness (Shore D) ASTM-D-2556
Gray	52	101	16	98

BD1691 super high temperature wear abrasion resistant metal repair agent epoxy compound curing features table(testing condition:temperature:25-30 degree,relative humidity:55)
Physical state	Operation time limit (25℃)	Usable time (25℃)	Working temperature (℃)	Density (g/cm3)
Paste	50 min	24 hours	-60-600	1.45

How to use:
1.Surface treatment:Do the coarsening treatment on the pending-repair or needing-bonding part,
then clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=3.5:1, make the A and B two components
mix uniformly,then use it up within specified operation time limit.

3.Coating: Make the mixed-up material be coating on the pending-repair part layer by layer,
the first layer should be compacted,make it infiltrate fully with the substrates.If the following working procedure
needs machining,should keep out appropriate machining allowance.

4.Curing:Curing for 2 hours at the temperature of 25-30 degree,then heat it up to the temperature of 80 degree
and keep this temperature for 2 hours,or it can be put into use after curing for 24 hours at the temperature of 25-30 degree,if the temperature is low,should heat it up or prolong curing time to promote the curing.

Transportation storage:
1.Sealed storage in the cool and dry place.The warranty period is 12 months.
2.Avoid placing it upside down,knocking against and transporting it as a non-dangerous product during transportation.

Packaging specification:
Two-component,250g/set,16 sets/carton.